| ʻAʻole. | Nā Waiwai Resin | Waiwai maʻamau | ʻĀpana | ʻAno Hoʻāʻo |
| 1 | Ka Umekaumaha Kūikawā, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Ka emi ʻana o ka ʻōpala, 23 ℃, 3.2mm, 23 ℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Ka helu kahe heheʻe, 220 ℃, 10kg | 22 | g/10min | ASTM D1238 |
| 4 | Ikaika Tensile ma ka Hua, 23 ℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Ka Elongation Tensile ma ka Hua, 23 ℃, 50mm/min, 3.2mm | 5 | %, (Min) | ASTM D638 |
| 6 | Ka Hoʻolōʻihi ʻana o ka Tensile i ka Haʻihaʻi, 23'℃, 50mm/min, 3.2mm | 10 | %, (Min) | ASTM D638 |
| 7 | Modulus Tensile, 23 ℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Ikaika Flexural, 23 ℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus Flexural, 23 ℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Ikaika hopena Izod, Notched, 3.2mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 11 | Ikaika hopena Izod, Notched, 3.2mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 12 | Ikaika hopena Izod, Notched, 6.4mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 13 | Ikaika hopena Izod, Notched, 6.4mm,-30 ℃ | 90 | J/m | ASTM D256 |
| 14 | Paʻakikī Rockwell, unahi-R | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, ʻAʻole i hoʻopili ʻia | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/h | 92 | °C | ASTM D1525 |
| 17 | Uila RTI | 95 | °C | UL 746B |
| 18 | ʻO ka mīkini RTI me ka hopena | 95 | °C | UL 746B |
| 19 | ʻO ka mīkini RTI me ka hopena ʻole | 95 | °C | UL 746B |
| 20 | Ka lapalapa ʻana, 1.5mm | HB | / | UL 94 |
| 21 | Ka lapalapa ʻana, 3.0mm | HB | / | UL 94 |