ʻO nā ʻāpana Polyamide 6—i ʻike nui ʻia ʻo Nylon 6 chips—ua kapa ʻia no nā loulou amide (–CO–NH–) i loaʻa i loko o kā lākou macromolecules. ʻIke pinepine ʻia he mau granules cylindrical keʻokeʻo, ʻo nā ʻāpana Nylon 6 he 210–220°C ka melting point a me ka mahana decomposition ma kahi o 300°C. Hiki ke hoʻoheheʻe ʻia i loko o ka phenol a me ka sulfuric acid i hoʻohuihui ʻia, hōʻike i nā waiwai insulation uila maikaʻi loa, a loaʻa iā lākou ke kūpaʻa maikaʻi i ka alkalis a me ka corrosion. ʻO Nylon ka mea kūpaʻa loa i ka abrasion o nā olonā synthetic āpau.
ʻO ka milo lole no nā lole, ka olonā ʻoihana a me ka olonā, nā ʻiliʻili Co-Extrusion.
Ka hoʻopili ʻana
ʻEke Jumbo 800Kg, 28MT/40HQ
Waiwai
ʻAno Hoʻāʻo
Nā Kūlana Hoʻāʻo
ʻĀpana
Hopena Hoʻāʻo
Papa Helu.
LX245 ʻĀlohilohi
ʻO ka mānoanoa pili
FZ/T 51004-2011
25℃, 96%H2SO4
/
2.50±0.03
Ka nui o ke kahe ʻana o ka nuipa heheʻe
GB/T 3682.1-2018
235℃, 2.16kg
g/10min
32.8
Ke kaumaha haki tensile
GB/T 1040.1-2022
50mm/min
MPa
67.45
Ka uhaki ʻana i ka elongation
GB/T 1040.1-2022
50mm/min
%
99.95
Ikaika kūlou
GB/T 9341-2008
2mm/min
MPa
89.99
Modulus Flexural
GB/T 9341-2008
2mm/min
MPa
2014.10
Ka ikaika hopena i hoʻopaʻa ʻia ʻo Izod
GB/T 1843-2008
23℃/5.5J
kJ/m²
3.16
Ka nui o ka wai
Q/1500LXJXA001-2023
/
%
0.038
Kiko heheʻe
Q/1500LXJXA001-2023
Ka helu hoʻomehana 10℃/min
℃
226.9
Ka nui o ka paʻa
GB/T 1033.1-2008
/
g/cm³
1.165
Hoʻokuʻu ʻōlelo:
ʻO nā helu ma luna nei he mau waiwai maʻamau no ka moʻo huahana like, i lawelawe ʻia ma ke ʻano he kuhikuhi no ke koho ʻana o ka mea kūʻai aku i nā huahana, a ua kau ʻia nā waiwai maoli i ka COA o ka huahana.